LR-F5400 Фторсиликоновая резина серии High Resilience

Он обладает отличной маслостойкостью, стойкостью к растворителям, низким уровнем сжатия, хорошей устойчивостью к высоким или низким температурам и упругостью.

Этот продукт представляет собой однородную смесь, изготовленная на основе фторсиликонового эластомера путем добавления некоторых видов наполнителей, добавок и т. Д.


Description of LR-F5400 High Resilience Series Fluorosilicone Rubber


Chemical Name

High Resilience Series Fluorosilicone Rubber

Synonyms

Fluorosilicone gum

Equivalents



Typical Technical Properties of LR-F5400 High Resilience Series Fluorosilicone Rubber


Test Item

Standard

Test Method

LR-5430

LR-5440

LR-5450

LR-5460

LR-5470

LR-5480

Appearance

Visual

Milk white, translucent

Pale yellow

Specific Gravity (g/cm3)

ASTM D792

1.38

1.41

1.42

1.43

1.45

1.47

Hardness / shoreA

ASTM D2240

28

40

48

60

70

80

Tensile Strength (MPa)

ASTM D412

10.2

9.5

9.5

10.2

9.9

8.1

Elongation At Break (%)

ASTM D412

485

494

363

296

241

159

Tear Strength (KN/m)

ASTM D624-B

18

26

19

22

21

16

Resilience (%)

ASTM D1054

41

35

46

40

37

39

*Heat Resistance

225°C X 72h

Hardness change / shore A

2

2

3

2

2

3

Tensile strength change %

-18

-17

-21

-25

-20

-19

Elongation at break change %

-19

-16

-18

-21

-16

-15

Fuel C

Volume change/%

23°C/72h

ASTM D471

22

19

18

19

19

19

Curing Condition

0.7 DBPH, Press cure: 170°C x 15min, Post cure: 200°C x 4h

The above values are not intended for use in preparing specifications.

Heat resistance additives need to be added to meet the requirements of heat resistance.


Processing Advice of LR-F5400 High Resilience Series Fluorosilicone Rubber


  • It is recommended to use 0.6 ~ 1 phr. 2,5-Dimethyl-2,5-di(tert-butylperoxy)hexane(DBPH).

  • The customer shall decide the optimum curing temperature and time according to the product dimensions and curing methods.


Package &Storage of LR-F5400 High Resilience Series Fluorosilicone Rubber


  • Packed in plastic bags placed into reinforced cardboard boxes. Each box contains 2 bags with 10kg per bag.

  • Keep in cool, dry and ventilated place. Keep away from sunlight and fire sources. This product has cold-flow characteristics, should avoid bag breakage in the process of transportation and usage, shelf life is 12 months from the date of production. It is shipped as non-hazardous substance.

Ваш профессиональный поставщик силанов & силиконов
Ваш профессиональный поставщик силанов & силиконов
Nanjing Silfluo New Material Co., Ltd.
Свяжитесь Нас
Попробуйте наше самое лучшее для удовлетворения ваших потребностей
Какие новости в Silfluo
Авторские права © Nanjing Silfluo New Material Co., Ltd. Все права защищены.
inquiry@silfluo.com
0086-18351817618